Fact Snapshot
- Paper: Compare study CaCO3 crystals on the cellulose substrate by microwave-assisted method and ultrasound agitation method
- Equipment: XH-100A
- Source: Ultrasonics Sonochemistry, 2012
- Research direction: sonochemistry
- Core conditions: Ultrasonic power 80 W, Microwave power 80 W, and Time 30 min / 4 min
Research Abstract
Compare study CaCO3 crystals on the cellulose substrate by microwave-assisted method and ultrasound agitation method was published in Ultrasonics Sonochemistry (2012) and is indexed as a Xianghu Q1 application case for XH-100A. The structured source links this paper to sonochemistry. Core operating conditions include Ultrasonic power 80 W, Microwave power 80 W, and Time 30 min / 4 min. The DOI recorded for this paper is 10.1016/j.ultsonch.2012.11.001.
Research Background and Problem
Equipment Use and Experimental Conditions
| Item | Parameter |
|---|---|
| Ultrasonic power | 80 W |
| Microwave power | 80 W |
| Time | 30 min / 4 min |
Evidence Details
Ultrasonic-method evidence: source values include 10 min, 600 nm, 20 min, 400 nm, 30 min, 320 nm.
Ultrasonic-method evidence: source values include 10 min, 56.3%, 20 min, 60.1%, 30 min, 83.3%.
Ultrasonic-method evidence: source values include 20 kHz, 80 W, 90 ± 2°C, 30 min, 4 min. Entities: JY92-2D.
Ultrasonic-method evidence: source values include 90%, 0.1 μg/mL, 90.96%, 500 μg/mL, 95.35%.
Microwave-method evidence: source values include 10 min, 0.82 μm, 20–30 min, 1.0–1.24 μm.
Microwave-method evidence: source values include 0.1 μg/mL, 93.28%, 500 μg/mL, 80.49%.
Ultrasonic-method evidence: source values include 82.2%, 800°C, 200–506°C, 65%.
Microwave-method evidence: source values include 92.7%, 200–506°C, 83.4%.
Ultrasonic-method evidence: source values include 90 ± 2°C, 30 min. Entities: XH-100B.
The pure phase of vaterite spheres with the diameter of about 320–600 nm were obtained by ultrasound agitation method, meanwhile, the mixed phases of calcite and vaterite with the diameter of about 0.82–1.24 μm were observed by microwave-assisted method.
Microwave-method evidence: source values include 468°C, 487°C.
Additional source evidence: source values include 10°C, 800°C. Entities: STA-409PC.
Ultrasonic-method evidence: source values include 1900 K.
Mechanism / Method Highlights
- Method context: Ultrasonic power 80 W, Microwave power 80 W, and Time 30 min / 4 min.
- Ultrasonic-method evidence: source values include 10 min, 600 nm, 20 min, 400 nm, 30 min, 320 nm
- Ultrasonic-method evidence: source values include 10 min, 56.3%, 20 min, 60.1%, 30 min, 83.3%
- Ultrasonic-method evidence: source values include 20 kHz, 80 W, 90 ± 2°C, 30 min, 4 min. Entities: JY92-2D
Application Value
- Positions XH-100A in a peer-reviewed Q1 research application.
- Records source affiliations: Beijing Forestry University.
Related Equipment
FAQ
Which Xianghu instrument is covered by this page?
What is the main application direction?
Which publication does this case come from?
Compare study CaCO3 crystals on the cellulose substrate by microwave-assisted method and ultrasound agitation method
Ultrasonics Sonochemistry, 2012
DOI: 10.1016/j.ultsonch.2012.11.001